| مكان المنشأ | شاندونغ، الصين |
| اسم العلامة التجارية | HAOBANG |
| إصدار الشهادات | ISO |
| رقم الموديل | 1.2mm tpo غشاء مقاوم للماء |
| Width | 1.2m/2.0m/3.0m |
| Color | White/Gray |
| Watertightness | 0.3 MPa, 2h Watertight |
| Heat Resistance | ≥70℃ |
| Application | airport, roof, workshop |
| Weatherability | Good |
| Coil Length | 20m or as agreed by both parties |
| Usage | Building Waterproof Material |
| Wind Uplift Resistance | 4.3 Kpa |
| Installation Method | Hot-air Welding |
| Product Name | 1.2mm TPO Roofing Membrane (Smooth Version) |
|---|---|
| Material | TPO |
| Color | White |
Haobang TPO-H is a uniform multi-layer composite thermoplastic polyolefin polymer waterproof membrane, which is made of thermoplastic polyolefin (TPO) material. It combines the weldability of propylene-alpha-olefin copolymer resins produced by advanced polymerization techniques with the durability of polypropylene resins. Through sophisticated processing technology, this membrane is specially applied to the detailed treatment of exposed roofs.
| Tensile Properties | Value |
|---|---|
| Tensile strength | ≥12 MPa |
| Elongation at rapture | 500% |
| Dimensional change rate on heating | 2% |
| Low temperature bending | -40℃ No Cracks |
| Watertightness | 0.3 MPa, 2h Watertight |
| Impact resistance | 0.5 kg*m, No water leakage |
| Peel strength at joints | 4.0 N/mm or damaged |
| Right angle tear strength | 60 N/mm |
| Water Absorption Rate (70℃168h) | 4% |
| Time | 672 h |
| Appearance | No blistering, cracks, delamination, sticking or voids |
| Tensile strength retention | ≥90% |
| Elongation retention at rapture | ≥90% |
| Low temperature bendability | -40℃, No Cracks |
| Appearance | No blistering, cracks, delamination, sticking or voids |
| Tensile strength retention | ≥90% |
| Elongation retention at rapture | ≥90% |
| Low temperature bendability | -40℃, No Cracks |
| Time | 2500 h |
| Appearance | No blistering, cracks, delamination, sticking or voids |
| Tensile strength retention | ≥90% |
| Elongation retention at break | ≥90% |
| Low temperature bendability | -40℃, No Cracks |
| Wind uplift resistance | 4.3Kpa |
Every standard roll is separately enclosed in polyethylene packaging. The width measures 2.0 meters, and the length is determined by the membrane's thickness.